chemical cross-linked heat shrinkable tube

heat shrinkable tube Feature: 1.Material:polyolefin 2.shrink temperature: 90 3.Temperature Renge :-55-125 heat shrinkable tube:Instr: shrink temperature:  90oC

Temperature Renge :-55-125

Radial Shrinking Ratio :   ≥50%

longitudinal shrinking ratio :    ≤5%

Tensile Strength  :   ≥14Mpa

Aging    :  158.0±1.0°Lays aside for 7 days 7Days Air Cren at158.0±1.0 Through

       134.0±1.0°Lays aside for 60 days 60Days Air Cren at134.0±1.0

Tensile Stength after Aging   : ≥10Mpa

Elongation after Aging  :  ≥200%

Volume Resistivity  :≥10Ω·cm

Dielectric strength  :≥25KV/mm

Flammability  : VW-1

Product specification	Before the contraction(mm)		After the contraction(mm)		Standard packing
	Minimum inside diameter	Wall thickness	Maximum inside diameter	Wall thickness
φ0.8	1.00±0.30	0.18	0.4	0.33	200
φ1.0	1.50±0.30	0.18	0.5	0.33	200
φ1.5	2.00±0.30	0.18	0.75	0.36	200
φ2.0	2.50±0.30	0.25	1	0.43	200
φ2.5	3.00±0.30	0.25	1.25	0.43	200
φ3.0	3.50±0.30	0.25	1.5	0.43	200
φ3.5	4.00±0.30	0.25	1.75	0.43	200
φ4.0	4.50±0.30	0.25	2	0.43	200
φ5.0	5.50±0.30	0.25	2.5	0.43	100
φ6.0	6.50±0.30	0.25	3	0.56	100
φ7.0	7.50±0.30	0.3	3.5	0.56	100
φ8.0	8.50±0.30	0.3	4	0.56	100
φ9.0	9.50±0.30	0.3	4.5	0.56	100
φ10.0	10.50±0.50	0.3	5	0.56	100
φ11.0	11.50±.50	0.3	5.5	0.56	100
φ12.0	12.50±0.50	0.3	6	0.56	100
φ13.0	13.50±0.50	0.35	6.5	0.69	100
φ14.0	14.50±0.50	0.35	7	0.69	100
φ15.0	15.50±0.60	0.35	7.5	0.69	100
φ16.0	16.50±0.60	0.35	8	0.69	100
φ17.0	19.00±0.60	0.4	9	0.76	100
φ18.0	21.00±0.60	0.4	10	0.76	100
φ20.0	23.00±0.70	0.45	11	0.89	100
φ22.0	26.00±0.70	0.45	12.5	0.89	50
φ28.0	29.50±0.70	0.45	14	0.89	50
φ30.0	31.5±0.70	0.45	15	0.89	50
φ35.0	36.00±0.70	0.5	17.5	0.89	50
φ40.0	40.70±0.70	0.5	20	0.89	50
φ50.0	50.70±0.70	0.5	25	1	50

ApplicationHeat Shrinkable Tube forms by chemical cross-linked (byradiation) thermally stabilized flame retarded polyolefin. It has excellent un-flammability, flexibility,and insulation.The shrinking temperature is very low and it can shrink very quickly.

It is widely used for various electric insulation and bonding of cales and connectors and applied for connecting end handling of electric wire, insulating and harness of electric wire.

chemical cross-linked heat shrinkable tube